Abstract To obtain a healthy human being with beneficial micro flora against different pathogenic infections, classical antibiotics with nanosized biomaterials were used to inhibit the growth of bacterium by their potent synergistic effect. Hence, this study planned to load an oxazolidinone antibiotic named linezolid (LD) onto functionalized chitosan (CN) with 3, 5- dinitrosalyslic acid (DA) via microwave synthesis without harsh condition.The exploring synergistic effect of linezolid (LD) with CN/DA controllable nanostructure was compact efflux-mediated methicillin-resistant Staphylococcus aureus (MRSA) burden and other selected bactericide Gram-positive ((S. aureus), Gram-negative (E. coli), Fungi (C. albicans), Yeast (A. niger), and E. faecalis.The obtained results showed that LD was incorporated into both the internal and external surface of the aggregated CN/DA nanosystem with an average diameter of 150 nm ± 4 hints of the drug loading. Owing to the nature of functionalized CN, the release efficiency attains 98.4% within 100 min. The designed LD@CN/DA exhibited inhibition zone 54 mm,59 mm, 69 mm, 54 mm, 57 mm, and 24 mm against the tested microbes respectively rather than individual LD.The major target of the current research is achieved by using LD@CN/DA as a nanoantibiotic system that has exceptional consistently active against multi-resistant pathogens, in between MRSA which resist LD |